High-Performance Near-IR Photodiodes: A Novel Chemistry-Based Approach to Ge and Ge–Sn Devices Integrated on Silicon

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

7 Author(s)
Roucka, R. ; Dept. of Chem. & Biochem., Arizona State Univ., Tempe, AZ, USA ; Mathews, J. ; Weng, C. ; Beeler, R.
more authors

Ge/Si heterostructure diodes based on n++Si(100)/i-Ge/p-Ge and p++Si(100)/i-Ge/n-Ge stacks and intrinsic region thickness of ~350 and ~900 nm, respectively, were fabricated using a specially developed synthesis protocol that allows unprecedented control of film microstructure, morphology, and purity at complementary metal-oxide-semiconductor compatible conditions. From a growth and doping perspective, a main advantage of our inherently low-temperature (390°C) soft-chemistry approach is that all high-energy processing steps are circumvented. Current-voltage measurements of circular mesas (60-250 μm in diameter) show dark current densities as low as 6 ×10-3 A/cm2 at -1 V bias, which is clearly improved over devices fabricated under low thermal budgets using traditional Ge deposition techniques. Spectral photocurrent measurements indicate external quantum efficiencies between 30 and 60% of the maximum theoretical value at zero bias, and approaching full collection efficiency at high reverse biases. The above Ge devices are compared to analogous low-temperature-grown (350°C) Ge0.98Sn0.02 diodes. The latter display much higher dark currents but also higher collection efficiencies close to 70% at zero bias. Moreover, the quantum efficiency of these Ge0.98Sn0.02 diodes remains strong at wavelengths longer than 1550 nm out to 1750 nm due to the reduced band gap of the alloy relative to Ge.

Published in:

Quantum Electronics, IEEE Journal of  (Volume:47 ,  Issue: 2 )