Performance of silicone rubber in DC inclined plane tracking tests

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

3 Author(s)
Bruce, G.P. ; Sch. of Electr. & Electron. Eng., Univ. of Manchester, Manchester, UK ; Rowland, S.M. ; Krivda, A.

The inclined plane tracking and erosion test IEC-60587 is not specified for DC testing. A dc test has been developed from the current ac standard and three formulations of silicone rubber tested. These materials were tested under three voltage levels (2.3, 2.7 and 3.2 kV) for both polarities. Positive dc tests have the highest average and peak leakage current and exhibit a higher degree of surface damage. The observed surface degradation pattern is heavily dependant on polarity. Consistently higher levels of erosion have been observed in the higher voltage positive cases. Erosion of the surface always starts at the bottom electrode, and spreads toward the top electrode. Puncturing of the 6 mm thick samples or deep erosion over more than half the distance between electrodes has only been observed under 2.7 and 3.2 kV positive polarity tests. Results have been analysed using a variety of leakage current analysis techniques going beyond the criteria specified in the original ac standard. The low-frequency behaviour of the leakage current was monitored using a 15 sample per second current recorder. The leakage current magnitude is investigated in a case study and is shown to follow a normal distribution. Reversing the polarity of tests shows the leakage current seen in a test is largely independent of the surface degradation pattern present, but the surface degradation pattern over the first three hours may dictate the morphology of ensuing deep erosion.

Published in:

Dielectrics and Electrical Insulation, IEEE Transactions on  (Volume:17 ,  Issue: 2 )

Date of Publication:

April 2010

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.