Static and dynamic magnetic properties of monodispersed Mn0.5Zn0.5Fe2O4 nanomagnetic particles

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $31
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

2 Author(s)
Parekh, Kinnari ; Department of Physics, Indian Institute of Technology Gandhinagar, Chandkheda, Ahmedabad 382 424, India ; Upadhyay, R.V.

Your organization might have access to this article on the publisher's site. To check, click on this link: 

Static and dynamic magnetic properties of oleic acid/oleyamine coated Mn–Zn ferrite nanoparticles of diameter 82 Å are reported. The zero-field-cooled peak temperature decreases with increasing magnetic field and obeys the well known de Almeida–Thouless line. The zero-field-cooled magnetization data are simulated by assuming noninteracting magnetic particles with uniaxial anisotropy and lognormal particle size distribution. The relevant parameters give the values of particle diameter (D) 80 Å, standard deviation 0.3 in ln(D), and the anisotropy constant K to be 5.8×105 erg/cm3. The observed higher value of standard deviation is due to the interparticle interaction. The complex magnetic susceptibility was measured as a function of temperature for frequencies ranging from 67 to 1800 Hz. The temperature at which the maximum in the ac-susceptibility curve is observed is well accounted by the Vogel–Fulcher law for both χ and χ. The peak is also observed in a plot of χ versus temperature, which may mean the existence of magnetic aftereffect, and furthermore, it has an Arrhenius as well as Vogel–Fulcher law type dependence. An observed nonthermal activation type relaxation mechanism at 12 K is attributed to possible quantum tunneling effect in Mn–Zn ferrite nanoparticles.

Published in:

Journal of Applied Physics  (Volume:107 ,  Issue: 5 )

Date of Publication:

Mar 2010

Need Help?

IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.