A complex x-ray structure characterization of Ge thin film heterostructures integrated on Si(001) by aspect ratio trapping and epitaxial lateral overgrowth selective chemical vapor deposition techniques

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

The purchase and pricing options are temporarily unavailable. Please try again later.
5 Author(s)
Zaumseil, P. ; IHP, Im Technologiepark 25, 15236 Frankfurt (Oder), Germany ; Schroeder, T. ; Park, Ji-Soo ; Fiorenza, J.G.
more authors

Your organization might have access to this article on the publisher's site. To check, click on this link: 

The development of Ge thin film substrates with low defect densities is of interest for future microelectronics as well as photovoltaics. This paper presents a complex x-ray characterization of Ge heterostructures, which were integrated on patterned Si(001) substrates using “aspect ratio trapping (ART)” and “epitaxial lateral overgrowth (ELO).” In both cases, thermal SiO2 layers were patterned into trenches with appropriate aspect ratio to confine misfit dislocations. In the case of ART Ge thin films grown in 180 nm spaced trenches, the x-ray characterization reveals that the Ge coalescence process between neighboring growth windows must be carefully controlled to avoid defect generation. In the case of ELO Ge heterostructures grown from trenches spaced by 20 µm, coalescence effects are clearly reduced but complications are detected in the form of lattice plane tilt in the ELO wings. Simulations are applied to unveil the influence of the different thermal expansion coefficients of Ge, Si, and SiO2 on the strain status of the ART and ELO Ge heterostructures.