Bonding-Failure Analysis with Electron Beam and Nuclear Scattering Techniques

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

3 Author(s)
Christou, A. ; Naval Research Laboratory; Code 5215; 4555 Overlook Ave., SW; Washington, DC 20375 USA. ; Nelson, G. ; Day, H.M.

Failure mechanisms related to gold bonding were determined using the scanning electron microscope, Auger electron spectroscopy, X-ray energy dispersive spectroscopy, electron microprobe analysis, and deuteron probe analysis. Power transistors from different lots were analyzed; there were four types of bond defects. Type I defect is darkened carbon inclusions in the bond area. Type II defect is a carbon buildup region on the posts probably in the form of graphite particles which adhered to the gold plating during processing. Type III defects are adsorbed carbon surface films. Type IV defects are gross discontinuities in the gold plating. Auger electron spectroscopy analysis and electron probe analysis proved that defects I, II, and III are subsurface and that further exposure to time-temperature and stress will result in carbide precipitates and hence cracks at the interface. Deuteron probe (DP) analysis of the same bond area has shown the presence of subsurface carbon (the predominant contaminant) thus verifying the Auger results. Contaminants such as manganese, iron boron, cobalt, nickel, chlorine, and sulfur were detected by energy dispersive X-ray analysis in concentrations of 100 ppM or more. These contaminants result in microcracks and voids which are formed by a time-temperature process. All bond-pull data had a bimodal distribution similar to that reported by Horsting. The bimodal distribution of pull-strength, carbon subsurface inclusions, and excessively high levels of contamination (from the plating bath), all indicate that a contamination-related failure mode exists.

Published in:

Reliability, IEEE Transactions on  (Volume:R-29 ,  Issue: 3 )

Date of Publication:

Aug. 1980

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.