The influence of Sn doping on the growth of In2O3 on Y-stabilized ZrO2(100) by oxygen plasma assisted molecular beam epitaxy

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $31
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

10 Author(s)
Bourlange, A. ; Department of Chemistry, Chemistry Research Laboratory, Mansfield Road, Oxford OX1 3TA, United Kingdom ; Payne, D.J. ; Palgrave, R.G. ; Zhang, H.
more authors

Your organization might have access to this article on the publisher's site. To check, click on this link:http://dx.doi.org/+10.1063/1.3153966 

The influence of Sn doping on the growth of In2O3 on Y-stabilized ZrO2(100) by oxygen plasma assisted molecular beam epitaxy has been investigated over a range of substrate temperatures between 650 and 900 °C. The extent of dopant incorporation under a constant Sn flux decreases monotonically with increasing substrate temperature, although the n-type carrier concentration in “overdoped” films grown at 650 °C is lower than in films with a lower Sn concentration grown at 750 °C. The small increase in lattice parameter associated with Sn doping leads to improved matching with the substrate and suppresses breakup of the films into square islands observed in high temperature growth of undoped In2O3 on Y-stabilized ZrO2(100). Plasmon energies derived from infrared reflection spectra of Sn-doped films are found to be close to satellite energies in core level photoemission spectroscopy, but for a nominally undoped reference sample there is evidence for carrier accumulation at the surface. This influences both the In 3d core line shape and the intensity of a peak close to the Fermi energy associated with photoemission from the conduction band.

Published in:

Journal of Applied Physics  (Volume:106 ,  Issue: 1 )

Date of Publication:

Jul 2009

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.