Fabrication and analysis of record high 18.2% efficient solar cells on multicrystalline silicon material

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

4 Author(s)
Rohatgi, A. ; Univ. Center of Excellence in Photovoltaic Res. & Educ., Georgia Inst. of Technol., Atlanta, GA, USA ; Narasimha, S. ; Kamra, S. ; Khattak, C.P.

Solar cell efficiencies of 18.2% (1 cm/sup 2/ areas) have been achieved using a process sequence which involves impurity gettering on 0.65 /spl Omega/-cm multicrystalline silicon (mc-Si) grown by the heat exchanger method (HEM). This represents the highest reported solar cell efficiency on mc-Si to date. Photoconductive decay (PCD) measurements were used to monitor the lifetime in control samples which underwent the same process sequence as solar cells. PCD analysis reveals that HEM mc-Si material with an average as-grown bulk lifetime (/spl tau//sub b/) of 12 /spl mu/s can achieve a lifetime as high as 135 /spl mu/s by process-induced gettering. Internal quantum efficiency (IQE) measurements reveal that the effective diffusion length (L/sub eff/) in the finished devices is 244 /spl mu/m (or close to 90% of the total device width). Detailed cell analysis shows that for this combination of /spl tau//sub b/ and L/sub eff/, the back surface recombination velocity (S/sub b/) of 10 000 cm/s or higher is the dominant efficiency limiting factor in the uniform regions of these mc-Si devices. Lowering S/sub b/ can raise the efficiency of untextured HEM mc-Si solar cells above 19.0%, thus closing the efficiency gap between good quality, untextured single crystal and mc-Si solar cells.

Published in:

Electron Device Letters, IEEE  (Volume:17 ,  Issue: 8 )

Date of Publication:

Aug. 1996

Need Help?

IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.