Structural and Electrical Properties of Mn-Doped  \hbox {Bi}_{4}\hbox {Ti}_{3}\hbox {O}_{12} Thin Film Grown on  \hbox {TiN}/\hbox {SiO}_{2}/\hbox {Si} Substrate for RF MIM Capacitors

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$33 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

8 Author(s)
Joo-Young Choi ; Dept. of Mater. Sci. & Eng., Korea Univ., Seoul, South Korea ; Lee-Seung Kang ; Kyung-Hoon Cho ; Tae-Geun Seong
more authors

Mn-doped Bi4Ti3O12 (M-B4T3) films were well formed on a TiN/SiO2/Si substrate at 200degC without buckling using RF magnetron sputtering. The leakage current density of these films was considerably influenced by the oxygen partial pressure (OPP), which was attributed to the presence of oxygen vacancies or oxygen interstitial ions. The film grown under 2.8-mtorr OPP showed the lowest leakage current density. The M-B4T3 films grown at 200degC showed a high dielectric constant of 38 with a low loss in both kilohertz and gigahertz ranges. The 39-nm-thick film showed a high capacitance density of 8.47 fF/mum2 at 100 kHz, and its temperature and quadratic voltage coefficients of capacitance were low at approximately 370 ppm/degC and 667 ppm/V2, respectively, with a low leakage current density of 7.8 times 10-8 A/cm2 at 2 V. Therefore, the M-B4T3 thin film grown on a TiN/SiO2/Si substrate is a good candidate material for high performance, radio frequency metal-insulator-metal capacitors.