Thermal annealing effect on magnetic properties of Fe nanoparticles implanted in yttrium-stabilized zirconia

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $31
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

6 Author(s)
Zhu, Xiaobin ; Department of Physics, University of Alberta, Edmonton, Alberta T6G 2J1, Canada ; Blois, C. ; Buchanan, K.S. ; Liu, Z.
more authors

Your organization might have access to this article on the publisher's site. To check, click on this link: 

The magnetic properties of thermally annealed Fe nanocrystals prepared through ion implantation in single crystal yttrium-stabilized zirconia (Y0.2Zr0.8O19) were studied by quasistatic hysteresis loop measurements and by pulsed ferromagnetic resonance. The change of coercivity and the shape of hysteresis loops at different annealing temperature can be interpreted through the size increase of the nanocrystals. Magnetostatic coupling must be taken into account to understand the rise times of the ferromagnetic resonance, especially for the samples annealed at higher temperature.