Ferroelectric-relaxor behavior of Ba(Ti0.7Zr0.3)O3 ceramics

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $31
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

4 Author(s)
Yu, Zhi ; Materials Research Laboratory, The Pennsylvania State University, University Park, Pennsylvania 16802 ; Ang, Chen ; Guo, Ruyan ; Bhalla, A.S.

Your organization might have access to this article on the publisher's site. To check, click on this link: 

Ferroelectric-relaxor behavior of Ba(Ti0.7Zr0.3)O3 ceramics is studied in the temperature range from 150 to 450 K. A broad dielectric peak with a high-dielectric maximum exhibits frequency dispersion. The dielectric relaxation rate follows the Vogel–Fulcher relation with E=0.21 eV and TVF=199.6 K. The polarization hysteresis loops were observed with a remnant polarization of 10 μC/cm2 at 175 K. The high-dielectric constant and high-polarization properties are expected to find practical applications at low temperatures. © 2002 American Institute of Physics.

Published in:

Journal of Applied Physics  (Volume:92 ,  Issue: 5 )