Plasma silicon oxide–silica xerogel based planar optical waveguides

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $31
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

4 Author(s)
Ponoth, Shom S. ; Department of Chemical Engineering, Rensselaer Polytechnic Institute, 110 8th Street, Troy, New York 12180 ; Agarwal, Navnit T. ; Persans, Peter D. ; Plawsky, Joel L.

Your organization might have access to this article on the publisher's site. To check, click on this link:http://dx.doi.org/+10.1116/1.1701847 

In this study, silica xerogels are used as the cladding for high-refractive-index-contrast waveguide systems. Silicon oxide, due to its relatively low refractive index, is an extensively used cladding material. The lower-refractive-index silica xerogel films enable us, to report losses for planar-slab waveguide systems with silicon oxide as the core. A spin-on sol-gel process was used for the silica xerogel deposition. The silicon oxide core was deposited using plasma enhanced chemical vapor deposition (PECVD), with silane and nitrous oxide as the reactive gases. Slab waveguides systems with core thickness of 1 μm and refractive-index contrast (Δn) as high as 0.35 were fabricated. With regard to the PECVD process, a deposition temperature of 150 °C enabled a stable structure, however, unacceptably high optical losses of 7±1.01 dB/cm at a wavelength of 650 nm and 5.59±0.69 dB/cm at 830 nm were measured using a prism-coupler based setup. On increasing the deposition temperature of the silicon–oxide film to 225 °C, the losses decreased to 0.98±0.73 dB/cm at 650 nm and 0.69±0.46 dB/cm at 830 nm. The decrease in the losses resulting from increasing the deposition temperature provided the motivation to develop deposition conditions to reduce stress in the silicon–oxide films at higher deposition temperatures for improved stability on xerogel films. Reduction in the silicon–oxide film stress was achieved by varying the silane and nitrous oxide flow rates. The deposition stress in the film was reduced from ∼460 to ∼240 MPa, mainly by increasing the silane flow rate. The silicon oxide with the reduced stress was stable on xerogel film with porosities as high as 56%, even though a deposition temperature of 300 °C was used. However, the slab waveguide stack using the low-stress silicon oxide exhibited an optical loss of 1.81±0.18 dB/c m at 650 nm and 1.41±0.27 dB/cm at 830 nm. The higher loss, as compared to that obtained for the higher-stress film deposited at 225 °C, is attributed to scattering from the columnar structure of the lower-stress silicon–oxide film. © 2004 American Vacuum Society.

Published in:

Journal of Vacuum Science & Technology B: Microelectronics and Nanometer Structures  (Volume:22 ,  Issue: 3 )

Date of Publication:

May 2004

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.