Magneto-optical properties of MnBi1-xSbx films

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

4 Author(s)
Celinski, Z. ; Opt. Sci. Center, Arizona Univ., Tucson, AZ, USA ; Pardo, D. ; Engel, Brad N. ; Falco, Charles M.

We have grown MnBi1-xSbx alloy films on mica and glass substrates under UHV conditions, and performed a systematic study of the structural, magnetic and magneto-optic properties on films in the concentration range 0⩽x⩽0.4. Sharp Reflection High Energy Electron Diffraction (RHEED) patterns were observed for samples grown on mica substrates, indicating epitaxial growth. X-ray diffraction patterns of MnBi1-xSbx grown on glass substrates show these films to be highly textured, with the c-axis parallel to the substrate normal. We found that only samples with Mn concentration above 50 at.% exhibited good magneto-optical properties. Perpendicular magnetization and Kerr rotation larger than 0.5° were observed for samples with Sb concentration less than 8 at.% in mica and 4 at.% on glass. For larger concentrations of Sb, the coercivity increased rapidly while Kerr rotation decreased. Samples grown on both types of substrates showed an increase in the Kerr rotation and ellipticity with decreasing light wavelengths. The off-diagonal E-field reflectivity, rxy, which describes the magneto-optic efficiency of the sample, is larger than that reported for TbFeCo layers