Low temperature formation of C54–TiSi2 using titanium alloys

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $31
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

10 Author(s)
Cabral, C. ; IBM T.J. Watson Research Center, Yorktown Heights, New York 10598 ; Clevenger, L.A. ; Harper, J.M.E. ; dHeurle, F.M.
more authors

Your organization might have access to this article on the publisher's site. To check, click on this link:http://dx.doi.org/+10.1063/1.120401 

We demonstrate that the temperature at which the C49 TiSi2 phase transforms to the C54 TiSi2 phase can be lowered more than 100 °C by alloying Ti with small amounts of Mo, Ta, or Nb. Titanium alloy blanket films, containing from 1 to 20 at. % Mo, Ta, or Nb were deposited onto undoped polycrystalline Si substrates. The temperature at which the C49–C54 transformation occurs during annealing at constant ramp rate was determined by in situ sheet resistance and x-ray diffraction measurements. Tantalum and niobium additions reduce the transformation temperature without causing a large increase in resistivity of the resulting C54 TiSi2 phase, while Mo additions lead to a large increase in resistivity. Titanium tantalum alloys were also used to form C54 TiSi2 on isolated regions of arsenic doped Si(100) and polycrystalline Si having linewidths ranging from 0.13 to 0.56 μm. The C54 phase transformation temperature was lowered by over 100 °C for both the blanket and fine line samples. As the concentration of Mo, Ta, or Nb in the Ti alloys increase, or as the linewidth decreases, an additional diffraction peak appears in in situ x-ray diffraction which is consistent with increasing amounts of the higher resistivity C40 silicide phase. © 1997 American Institute of Physics.

Published in:

Applied Physics Letters  (Volume:71 ,  Issue: 24 )

Date of Publication:

Dec 1997

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.