Fatigue Behavior of Y–Ba–Cu–O/Hastelloy-C Coated Conductor at 77 K

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

2 Author(s)
Mbaruku, A.L. ; Dept. of Eng. Mater., Univ. of Dar es Salaam, Dar es Salaam ; Schwartz, J.

Superconducting materials are subjected to various loading in motors, transformers, generators, and other magnet applications. The loading conditions include bending, tension, compression, and fatigue, and result from coil manufacturing, thermal cycling, quenching, and normal operation. Each of these loading conditions can affect the performance of the superconductor and thus the magnet and system. It is important, therefore, to understand the electromechanical behavior of the superconducting material to optimize the design. Here we report the effects of mechanical fatigue at 77 K on the electrical transport properties of YBa2 Cu 3O7-delta/Hastelloy-C coated conductors. The effects of longitudinal tensile fatigue on the critical current and the n-value are reported. Strain controlled fatigue studies include strains up to 0.495% and strain ratios of 0.2 and 0.5. Scanning electron micrographs of the fatigued conductors are used to identify the sources of failure. Crack formation is believed to be the cause of I c degradation in fatigued samples. Further, the fatigue strength and ductility behaviors analyzed using a 5% reduction in I c as the electrical definition of failure showed that the fatigue strength exponent is within the values found for metals but both the fatigue ductility coefficient and exponent show that the material tested is brittle.