Unified Model of Damage Annealing in CMOS, from Freeze-In to Transient Annealing

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

2 Author(s)
Sander, H.H. ; Sandia Laboratories, Albuquerque, New Mexico 87115 ; Gregory, B.L.

Irradiation studies at 76°K are described which demonstrate that radiation-produced holes in SiO2 are immobile at this temperature. If an electric field of either polarity is present in the SiO2 during 76°K irradiation, to sweep out the mobile electrons, the holes will virtually all be trapped where created and produce a uniform positive charge density in the oxide. This predicts ¿VT ¿ dox2 , which is observed. The magnitude of the observed shift is consistent with 18 eV required per hole-electron pair generated. All CMOS transistors of the same oxide thickness exhibit the same initial ¿VT, for a given exposure level, regardless of oxide type or process. The rate of annealing differs, both as a function of oxidation process and oxide thickness. Thin oxides have two advantages: a smaller ¿VT (stable shift) and faster annealing. If a CMOS device is irradiated for sufficient time at 76°K to build in an appreciable field, further irradiation with zero gate-substrate bias will produce little additional change in VT, since the field in the oxide tends to keep all generated electrons in the oxide, where they recombine with trapped holes. Room temperature annealing following a pulsed gamma exposure occurs in two regimes. The first regime can be quite fast, and occurs prior to 10-4 seconds. The magnitude of this early-time recovery is both process dependent and thickness dependent.

Published in:

Nuclear Science, IEEE Transactions on  (Volume:22 ,  Issue: 6 )

Date of Publication:

Dec. 1975

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.