Fabrication of Bi/sub 2/Sr/sub 2/Ca/sub 2/Cu/sub 3/O/sub x/ thin film grain boundary junctions

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$33 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

7 Author(s)
K. Ohbayashi ; Res. & Dev. Center, NGK Spark Plug Co. Ltd., Nagoya, Japan ; H. Fujii ; A. Kuzuhara ; T. Ohtsuki
more authors

As-grown high-quality superconducting thin films of the Bi/sub 2/Sr/sub 2/Ca/sub 2/Cu/sub 3/O/sub x/ were prepared by RF magnetron sputtering with a regulated shuttering technique. 2223 phase films with a 2201 phase buffer layer were deposited on MgO (100) substrates under rigorous control of the bismuth content and valence. As a source of bismuth, Bi(metal) and Bi/sub 2/Sr/sub 2/CuO/sub x/ targets were used. At the preparation no post-treatment steps were performed. The zero resistivity critical temperature of the as-grown film was 107.3 K. Using these films, Bi/sub 2/Sr/sub 2/Ca/sub 2/Cu/sub 3/O/sub x/ step-edge and bicrystal Josephson junctions were prepared. At step-edge junctions, Josephson current was observed up to 41 K, below this temperature I-V curves were RSJ-like. On the other hand, bicrystal junctions were fabricated,on the bicrystal MgO (100) substrate with a misorientation angle of 24/spl deg/. Typical RSJ model I-V curves were observed up to 60 K. The modulation depth goes up to 90%. I/sub c/R/sub n/ values were about 1.0 mV at 4.2 K.<>