Nanopore foams of high temperature polymers

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

5 Author(s)
Labadie, J.W. ; IBM Almaden Res. Center, San Jose, CA, USA ; Hedrick, J.L. ; Wakharkar, V. ; Hofer, D.C.
more authors

A method of generating high-temperature polymer foams with pore sizes in the nanometer regime was developed. The nanofoams were prepared by casting a block copolymer comprising a thermally stable and a thermally labile block, followed by a subsequent thermal treatment to degrade the labile material and generate the pores. The morphology of the block copolymer film was made up of a high-temperature polymer matrix, with the labile component as the dispersed phase. Thermolysis of the labile block affords pores where the size and shape of the pores are dictated by the initial copolymer morphology. Nanopore foam formation is described for triblock copolymers of poly(phenylquinoxaline) (PPQ) with poly(propylene oxide) (PO) as the labile block. Foam formation led to a 10-15% reduction in density, consistent with the PO composition, and a dielectric constant as low as 2.3. SAXS and TEM measurements indicated pore sizes of approximately 10 nm

Published in:

Components, Hybrids, and Manufacturing Technology, IEEE Transactions on  (Volume:15 ,  Issue: 6 )