Low firing Y5V relaxor multilayer ceramic capacitors

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

2 Author(s)
Chen, G.-F. ; Dept. of Electr. Eng., Nat. Cheng Kung Univ., Tainan, Taiwan ; Shen-Li Fu

Low firing Y5V multilayer ceramic capacitors (MLC) based on the low firing dielectrics Pb(Fe/sub 2/3/W/sub 1/3/)/sub 0.41/(Fe/sub 1/2/Nb/sub 1/2/)/sub 0.49/Ti/sub 0.1/O/sub 3/ were fabricated. The prepared Y5V MLC can be sintered at temperatures of 870 to 930 degrees C. Such a low firing temperature makes it possible to use Pd/Ag (10/90) as the internal electrode. Consequently, capacitor cost becomes lower. The dielectric properties of a fabricated MLC change sharply with DC bias. A fabricated 0.33- mu F 1206 size 50-V Y5V MLC features high volumetric efficiency (110 mu F/cm/sup 3/), low-loss tangent, (or=10/sup 3/ M Omega ), low aging rate (or=25.5 kV/mm). Possible explanations for the effect of bias and frequency on the dielectric properties are given.<>