Effects of calcining and sintering parameters on the magnetic properties of high-permeability MnZn ferrites

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$33 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

4 Author(s)
Hua Su ; Sch. of Microelectron. & Solid-State Electron., Univ. of Electron. Sci. & Technol. of China, Chengdu, China ; Huaiwu Zhang ; Xiaoli Tang ; Xubo Wei

For asymmetric digital subscriber line (ADSL) technology applications, new MnZn ferrites are required with not only high initial permeability, but also with low hysteresis material constant ηB. The effects of calcining and sintering temperatures and oxygen equilibrium partial pressure on the magnetic properties of MnZn ferrites are studied in this work. It was found that raising the calcining temperature required a rise in the sintering temperature to simultaneously achieve maximum permeability and the lowest ηB value. Both grain size and porosity had an effect on the initial permeability of the samples. Porosity had an even larger effect on the ηB value than the initial permeability. Oxygen equilibrium partial pressure also had an important effect on the initial permeability and ηB value. In our testing range, both the initial permeability and the ηB value decreased with increasing value of A (oxygen parameter). In order to optimize synthesis conditions for the high initial permeability and low ηB value, it was best to calcine the sample at 950°C and sinter it at 1370°C, with A=7.55.