Compositional dependence of magnetoresistance in TbFeCo amorphous film

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

4 Author(s)
Rahman, M.Tofizur ; Dept. of Inf. Eng., Shinshu Univ., Nagano, Japan ; Xiaoxi Liu ; Matsumoto, Mitsunori ; Morisako, A.

The dependence of Tb and Co concentration on the magnetoresistance (MR) of TbFeCo amorphous films with perpendicular magnetic anisotropy have been studied at room temperature. TbxFe(88-x-y)Coy films (where x=15--37 at% and y=5--25 at%) with thickness of 200 nm are deposited by dc-magnetron sputtering. The MR ratio is sensitively dependent on the Tb concentration. The MR ratio is increased up to about 2.8% for a Tb concentration of about 22.4 at% then decreased for more Tb content. No significant effect of Co concentration on the MR ratio has been observed. The relation between MR ratio and film composition can be ascribed to the dependence of the domain wall width on the film concentration. The domain wall width decreases with an increase in Tb concentration and again increases for more Tb content showing its minimum value at about 22.4 at % of Tb concentration. It may be considered that the observed MR is contributed from the domain wall.

Published in:

Magnetics, IEEE Transactions on  (Volume:41 ,  Issue: 10 )