Integration issues of Crx(SiO)1-x on-chip resistors

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

2 Author(s)
Fan Wu ; Microelectron. Center, Medtronic Inc., Tempe, AZ, USA ; Morris, J.E.

On-chip passives are the best solution for very high component density with increased electrical performance, improved reliability, reduced size, weight and lower cost. The on-chip passives and elimination of surface mount technology will lead to the reduction of overall part count, elimination of solder joints, improvement of wireability, and improved high frequency behavior due to reduction of parasitic inductance. High resistivity on-chip resistor is crucial for low power applications, such as implantable medical devices and portable electronic devices. Crx(SiO)1-x system is a cermet material, which can be deposited as an on-chip thin film resistor with the highest resistivity among all the thin film resistor materials. Two of the main challenges for on-chip resistor manufacturing are 1) compatibility to the planar silicon process and 2) reproducibility. Among all the factors that affect the compatibility and reproducibility, substrate effect and contact resistance are two significant and important one because different materials, such as thermally grown SiO2, CVD deposited Si3N4, PSG, and BPSG, is used as substrates for the resistor films. And different metal, such as AlCuSi, Ti, and TiW are used as metallization materials. In this study the effects of different contact metal materials and processing parameters on the metal/resistor contact resistance were investigated. A bipolar process is used to fabricate aluminum to Crx(SiO)1-x contact, and a 0.6 mm BiCMOS process is used to fabricate Titanium to Crx(SiO)1-x contact. TEM and AFM were used to study the morphological and metallurgical changes prior and post annealing. The study shows that 1) Ti contact has lower contact resistance and higher stability compared to AlCuSi contact. 2) The main factor on AlCuSi contact is the Al-Si alloy formation on the AlCuSi/ Crx(SiO)1-x contact. A TEM image of AlCuSi/ Crx(SiO)1-x contact post 450C/30 min anneal is shown.