Effect of pre-annealing temperature and atmosphere on the microstructure and transport property of Bi-2223/Ag tapes

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

3 Author(s)
Jiang, C.H. ; Nat. Inst. for Mater. Sci., Tsukuba, Japan ; Kumakura, H. ; Koizumi, T.

The phase assemblage and Bi-2212 texture in Bi-2223/Ag tapes before the heat treatment were varied by pre-annealing the tapes at different temperatures and in pure Ar or air for 10 h. Then all the tapes were isothermally heat treated at 840°C in air for 4 cycles with intermediate pressings. The Jc of the samples pre-annealed in pure Ar were lowered no matter which annealing temperature was used. The best Jc was obtained in the samples pre-annealed at 800°C in air, which was in an average value of 21.7 kA cm-2, being increased by 25% compared with that of the unannealed tapes (17.3 kA cm-2). The transport properties of various pre-annealed samples were correlated to the phase evolutions, growth and pre-alignment of Bi-2212 grains during pre-annealing.