Temperature-dependent I-V characteristics of organic-inorganic heterojunction diodes

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

3 Author(s)
Ahmed, M.M. ; Inst. of Eng. Sci. & Technol., Topi, Pakistan ; Karimov, Kh.S. ; Moiz, S.A.

In this paper, heterojunctions were fabricated by employing p-type Si and thin films of poly-N-epoxipropylcarbazole (PEPC) doped with tetracyanoquinodimethane (TCNQ). The PEPC films were grown on Si wafers at room temperature but with different gravity (g) conditions:-1, 123, 277, and 1107g. Current-voltage (I-V) characteristics of the grown hybrid structures were evaluated as a function temperature (T) ranging from 20°C to 60°C. It was found that all samples are p-p isotype heterojunctions and the junctions fabricated at a high value of g, i.e., at 277 and 1107 g, showed reversible rectifying properties as a function of device temperature. Whereas the behavior of devices fabricated at 123 and 1 g were rectifying at room temperature, but became almost nonconductive after treating the samples at 60°C. Rectification ratio, threshold voltage, reverse saturation current, and junction resistance of the fabricated junctions were evaluated at different temperatures. At T=60°C, the devices grown at 1107 g exhibited rectification ratio less than unity which may be attributed to the switching of the depletion at the interface. This has been explained by assuming the generation of carriers are at elevated temperatures in the organic film, and their subsequent emission from the organic to the inorganic side of the heterojunction.