Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

6 Author(s)
Horibe, M. ; Int. Supercond. Technol. Center, Supercond. Res. Lab., Tokyo, Japan ; Wakana, H. ; Ishimaru, Y. ; Adachi, S.
more authors

We have examined and optimized the fabrication conditions for multilayer structures needed in high-Tc single flux quantum circuits. La0.2Y0.9Ba1.9Cu3Ox (La-YBCO) was chosen as a material for both the groundplane (GP) and base-electrode. The GP-La-YBCO was deposited at 740°C by a sputtering method and the optimized 300 nm thick film exhibited a typical average roughness (Ra) of 2 nm. (La,Sr)2AlTaO6 (LSAT) isolation layer sputter-deposited under the same conditions as the GP-La-YBCO showed good crystallinity and a relatively flat surface (Ra∼2 nm). For the deposition of La-YBCO base electrode, a slightly lower substrate temperature (720°C) resulted in a smooth film surface (Ra∼2 nm), while higher substrate temperatures led to appearance of precipitates and hollows on the La-YBCO and columnar morphology of the LSAT layer which was revealed by cross-sectional SEM observation. Interface-engineered ramp-edge junctions fabricated on LSAT/GP-La-YBCO multilayer structures exhibited RCSJ-like I-V characteristics with typical IcRn products of 2 mV at 4.2 K. Excellent isolation between the GP and the base electrode better than 109 Ω/cm2 was also confirmed.

Published in:

Applied Superconductivity, IEEE Transactions on  (Volume:13 ,  Issue: 2 )

Date of Publication:

June 2003

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.