Reliability in InGaAsP/InP buried heterostructure 1.3 µm lasers

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

6 Author(s)
Mizuishi, K. ; Hitachi Ltd., Kokubunji, Tokyo, Japan ; Sawai, Masaaki ; Todoroki, Satoru ; Tsuji, S.
more authors

A study was conducted of aging-induced Sn whisker growth at the surface of Au-Sn bonding solder layers around a laser chip, as well as metallurgical reactions, especially in p-side down lasers, at the interface of the solder and laser crystal just below the active layer. These phenomena cause electrical shorts in InGaAsP/InP laser diodes, which occur suddenly in devices operated for long periods without any previous symptoms having appeared in their aging characteristics. To completely eliminate such failures, a novel assembling method in which chips were mounted p-side up on semiinsulating SiC submounts using Pb-Sn solder, was applied to InGaAsP/InP buried heterostructure (BH) lasers emitting at 1.3 μm. BH lasers assembled by this method do not suffer any shorting failure even after 8000 h operation under 60°C and 5 mW/facet output conditions. The small degradation rates obtained, for example, 3 percent/kh (median) at 60°C, certify the reliability of these improved lasers. As long as the stripe width of the active layer was optimized to be in the range of1.5-2.5 mum necessary for obtaining kink-free light output versus current properties, no detrimental changes in laser characteristics, including transverse and longitudinal modes and dynamic output response, were observed in aged lasers. In this paper, the long-term degradation modes observed are presented, and possible causes are discussed.

Published in:

Quantum Electronics, IEEE Journal of  (Volume:19 ,  Issue: 8 )

Date of Publication:

August 1983

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.