The magnetic properties of Co-Ni-Fe films

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

3 Author(s)
Lampert, R. ; Univac, Division of the Sperry Rand Corporation, St. Paul, Minn ; Gorres, J.M. ; Hanson, M.M.

H_{k} , \delta H_{k} ,\alpha _{90} and Hchave been measured for vapor-deposited nonmagnetostrictive Co-Ni-Fe films, 1500 Å thick. All parameters except Hchave been measured using the transverse-biased permeability apparatus. Hkincreases linearly with cobalt melt content up to 15-percent cobalt, \delta H_{k} and Hcincrease with increasing cobalt and substrate temperature. α90decreases in the region 0-15-percent cobalt and then increases with increased cobalt melt content and substrate temperature. The coefficient of magnetoelastic composition sensitivity S is the slope of the curve η versus the ratio of nickel to iron in the melt for a constant cobalt percentage about the point \eta = 0 . The value of S increases rapidly with substrate temperature to a maximum near 300°C if the cobalt percentage is small. For larger amounts of cobalt S is reduced and is more independent of temperature. It is proposed that the volume fraction and the mobility of the grain boundaries in the film structure are primarily responsible for S .

Published in:

Magnetics, IEEE Transactions on  (Volume:4 ,  Issue: 3 )