Magnetization reversal in films with biaxial anisotropy

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

1 Author(s)
Doyle, W.D. ; UNIVAC, Blue Bell, PA, USA

Two models of magnetization reversal for the case of films with biaxial anisotropy are considered: 1 ) the coherent rotation model of Stoner and Wohlfarth (S-W) and 2) the noncoherent or wall-motion model of Kondorsky (K). The former has been considered by several authors previously while the latter is developed in the present paper. The (K) model presumes that the anisotropy field is much larger than the critical field for wall motion and that only the component of the applied field perpendicular to the bisector of the initial and final positions of the magnetization is effective. It also presumes that whenever the effective component exceeds a certain critical field determined by the structure of the sample, the magnetization will switch. Rotational hysteresis, torque curves, and hysteresis loops observed on single-crystal cobalt films exhibiting biaxial crystalline anisotropy are compared with the predictions of both models. It is found that at low fields the (K) model is a much better description than (S-W) while at high fields the reverse is true. This behavior is analogous to the behavior of uniaxial polycrystalline films with low values ofH_{c}/H_{k}. This similarity and others suggest that the true reversal process is as complicated in single-crystal films as in polycrystalline films, and that dispersion in both the magnitude and direction of the anisotropy is present. Because the samples are single-crystal, single-element films, the possible causes of dispersion are reduced. The most likely cause is locally varying stresses arising from uneven substrate bonding.

Published in:

Magnetics, IEEE Transactions on  (Volume:2 ,  Issue: 2 )

Date of Publication:

Jun 1966

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.