Superconducting properties of thin film niobium carbonitrides on carbon fibers

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

4 Author(s)
Pike, G. ; Sandia Laboratories, Albuquerque, NM ; Mullendore, A. ; Schirber, J. ; Napier, J.

The characteristics of a new superconducting wire material, consisting of a 7 μm carbon filament substrate thinly coated with niobium carbonitride, are reported. These filaments are coated (∼ 1000 at a time as a yarn) by a co-CVD process in which the desired carbonitride is deposited as a compound. Several coating compositions from NbC to NbC.75N.15have been studied. At each composition several coating thicknesses from 300 to 3000 Å were prepared. Although our present coating compositions are not near NbC0.3N0.7, which has previously been determined as optimum for this pseudobinary system, we nevertheless have obtained excellent superconducting properties. Zero-field critical current densities of 2 × 106A/cm2in the coating have been obtained, and there is no discernable ac loss at frequencies up to 50 kHz. In addition to the superconducting measurements we have also performed chemical, x-ray diffraction, and electron microscopic analyses on the coated filaments.