Rotational power loss of silicon steel sheet

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$33 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

4 Author(s)
M. Enokizono ; Fac. of Eng., Oita Univ., Japan ; T. Suzuki ; J. Sievert ; J. Xu

Rotational power losses have been measured on nonoriented grain-oriented silicon steel sheets under different rotational flux conditions. Several methods have been proposed for this purpose. Among these, a method based on the measurement of the field quantities B x, By, Hx, and Hy seems to be the most convenient as far as the preparation of the test specimen is concerned. In this method, the rotational power loss Pr is measured as the torque loss generated from the angle of lag between the H-vector and the B-vector caused by the rotating field. The effect of the axis ratio of the rotational flux components and of the inclination angle of field strength relative to the rolling direction of a sample sheet on the rotational power loss was investigated with the method. This loss was compared with the conventional loss, which was shown as the sum of loss Pt in the x and y directions. Although in the nonoriented steel sheet Pt (conventional rotational loss) is larger than Pr , in the grain-oriented steel sheet Pt is smaller than Pr. When the field strength was applied in the nonoriented sheet at a 45° angle from the rolling direction of the sheet, the rotational power loss reached minimum values