Influence of phosphorus on undoped and zinc doped InGaAs

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

6 Author(s)
Karlina, L.B. ; A.F. Ioffe Physicotech. Inst., Acad. of Sci., St. Petersburg, Russia ; Ber, B.Ya. ; Blagnov, P.A. ; Boiko, A.M.
more authors

Simultaneous diffusion of P and Zn in In0.53Ga0.47As using Sn-InP-Zn as a dopant source is investigated. The dependence of the diffusion profiles Zn and P on diffusion time at 600°C is presented. Typical zinc concentration and depths obtained are 10*19 cm-3 and 0.5-1.3 μm. The incorporation of P into InGaAs at almost constant concentration for layers of 3-μm thickness was detected. The effects of the exposure of InGaAs to 1 MeV electron fluence 1015, 1016 cm-2 were investigated by photoluminescence and Raman scattering. Results presented here show a slight increase in PL emission after irradiation InGaAs (Zn, P) by fluence of 1015 cm-2. The free carrier concentration remains at the same level before and after irradiation.