Mixed rare-earth effects in (Sm/Gd)2(Fe/Si)17 intermetallics

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

10 Author(s)
Marasinghe, G.K. ; Dept. of Phys., North Dakota Univ., Grand Forks, ND, USA ; Priyantha, W. ; Kamaraju, K. ; James, W.J.
more authors

The effects of mixing samarium and gadolinium on the crystallographic and magnetic properties of SmyGd2-y Fe17-xSix (x=0, 0.33, 1.67) intermetallics have been investigated using X-ray diffraction techniques and SQUID and vibrating magnetometer measurements. The SmyGd2-yFe17-xSix samples, except for the sample with x=3 and y=1, crystallized in the rhombohedral Th2Zn17-structure with little or no impurities. For a given silicon content (fixed x), the unit volume and saturation magnetization increases at the approximate average rates of 4 Å 3 and 24 emu/g per substituted samarium atom, respectively. The Curie temperature (Tc) for a given silicon content, on the other hand, decreases with increasing samarium content at an average rate of 30-40°C per substitution. The affect of substituting silicon for iron on Tc is more marked, with Tc increasing at a rate of almost 70°C per silicon substitution at low silicon concentrations. For a given samarium content (fixed y), the unit cell volume and saturation magnetization decreases at approximate rates of 5 Å3 and 9 emu/g per substituted silicon atom, respectively. X-ray diffraction studies of magnetically aligned powders indicate that the easy direction of magnetization is in the basal plane of the rhombohedral unit cell. All of the samples were found to have very little magnetic anisotropy with no apparent dependence of the anisotropy on the samarium or silicon content. The 340°C Tc measured for the SmGdFe14Si3 sample is unusually high for these intermetallics and its XRD pattern is indicative of a phase other than the rhombohedral Th2Zn17-type