Investigations of failure mechanisms of TAB-bonded chips during thermal aging

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

2 Author(s)
Zakel, E. ; Tech. der Mikroperipherik, Tech. Univ., Berlin, Germany ; Reichl, H.

Eutectic soldering and thermocompression bonding were investigated with regard to thermal aging mechanisms in tape automated bonding (TAB) chips. These methods require two different metallurgies: Cu-Sn-Au and Cu-Au. Effects such as pore formation which are due to the Kirkendall effect and the formation of ternary phases were investigated. The influence of the lead roughness and of copper recrystallization was shown by the use of electrodeposited copper and rolled annealed copper. The influence of these parameters on long-term reliability is summarized. Results of the study include the following: the predominant failure mechanisms in a pull test was lead fracture. The results from the pull test show that the values are mainly affected by aging effects in the leads. Metallographic examinations show different aging mechanisms at the bonded interfaces. The Kirkendall effect and pore formation is accelerated by the accumulation of tin in the interface between copper and gold due to the high roughness of the tape. The formation of pores for eutectic soldering can be avoided by a tape with reduced roughness, which minimizes the accumulation of tin during the bonding process. Compared with other contact methods for chips, TAB technology shows high reliability, with very low degradation even after very severe thermal aging at 200°C

Published in:

Components, Hybrids, and Manufacturing Technology, IEEE Transactions on  (Volume:13 ,  Issue: 4 )

Date of Publication:

Dec 1990

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.