Structural, optical, and electrical properties of nanocrystalline silicon films deposited by hydrogen plasma sputtering

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $31
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

7 Author(s)
Garrido, B. ; Departament d’Electrónica, Universitat de Barcelona, Diagonal 645-647, 08028 Barcelona, Spain ; Perez-Rodrı guez, A. ; Morante, J.R. ; Achiq, A.
more authors

Your organization might have access to this article on the publisher's site. To check, click on this link: 

Nanocrystalline silicon films were deposited by radio frequency sputtering in a pure H2 plasma on glass and monocrystalline <100> silicon at various substrate temperatures, Ts. The detailed structural, optical, and electrical analysis of the films has been performed by transmission electron microscopy, Raman scattering, infrared spectroscopy, x-ray diffraction, optical absorption, photoluminescence and electrical measurements. The data obtained show that, to a significant extent, control of the structure and hence of the optical and electrical properties of the films can be achieved by changing Ts. Increasing Ts from 50 to 250 °C leads to an increase of the average grain size (from a few nm to a few tens of nm) and crystalline fraction (from 37% to 74%) and the optical band gap decreases from 2.40 to 1.95 eV. Hydrogen incorporation, together with Ts, are thought to be at the origin of the resulting microstructure and consequently determine the optical and transport properties. Moreover, hydrogen content was found to be associated with void formation which induces structure relaxation with very low residual stress. Finally, electrical conductivity in the layers increases by more than six orders of magnitude with Ts. The high dark conductivity measured from the sample deposited at the highest Ts (≫10-3 Ω-1cm-1) and its low activation energy (0.13 eV) are in agreement with the high crystalline fraction of this layer, where tunneling of carriers between the crystallites likely occurs. © 1998 American Vacuum Society.

Published in:

Journal of Vacuum Science & Technology B: Microelectronics and Nanometer Structures  (Volume:16 ,  Issue: 4 )