1.6 nm oxide equivalent gate dielectrics using nitride/oxide (N/O) composites prepared by RPECVD/oxidation process

Ultrathin nitride/oxide (/spl sim/1.5/0.7 nm) dual layer gate dielectrics have been formed using remote plasma enhanced CVD of nitride onto plasma-grown oxide interface layers. High accumulation capacitance (1.72 μF/cm
²
) is measured and the equivalent oxide thickness is 1.6 nm after quantum effect corrections. Compared to 1.6 nm oxides, a tunneling current reduction of more than 100 fold is found for devices with 1.6 nm N/O dielectrics due to increased film thickness and interface nitridation. Hole channel mobility decreases by about 5%, yielding very good P-MOSFET current drive. Excellent dielectric reliability and interface robustness are also demonstrated for P-MOSFET's with N/O dielectrics.