Thermal stability of IrO2 gate based AlGaN/GaN HEMT

We investigate a thermal stability of iridium oxide (IrO
2
) gate based AlGaN/GaN HEMT devices by using a long-term thermal stress at 300 °C and 450 °C for 48 hours in air atmosphere. AlGaN/GaN high electron mobility transistors with the gate contact based on IrO
2
were designed for high temperature applications. IrO
2
gate interfacial layer is formed by high temperature oxidation of 15nm thick Ir gate contact layer (T = 500 − 800 °C, for 1 min in O
2
ambience) to provide a high temperature stable gate interface. IrO
2
gate based AlGaN/GaN HEMT show excellent thermal stability after long-term storage tests at 450 °C for 48 hours in the air, and even leakage current of Schottky gate contacts is continual decreasing with the storage time. AlGaN/GaN HEMTs with Schottky gate contacts based on high temperature formed IrO
2
could be predetermined for sensing applications at high temperatures.