High-performance /spl lambda/=1.3 /spl mu/m InGaAsP-InP strained-layer quantum well lasers

Compressively and tensile strained InGaAsP-InP MQW Fabry-Perot and distributed feedback lasers emitting at 1.3-/spl mu/m wavelength are reported. For both signs of the strain, improved device performance over bulk InGaAsP and lattice-matched InGaAsP-InP MQW lasers was observed. Tensile strained MQW lasers show TM polarized emission, and with one facet high reflectivity (HR) coated the threshold currents are 6.4 and 12 mA at 20 and 60/spl deg/C, respectively. At 100/spl deg/C, over 20-mW output power is obtained from 250-/spl mu/m-cavity length lasers, and HR-coated lasers show minimum thresholds as low as 6.8 mA. Compressively strained InGaAsP-InP MQW lasers show improved differential efficiencies, CW threshold currents as low as 1.3 and 2.5 mA for HR-coated single- and multiple quantum well active layers, respectively, and record CW output powers as high as 380 mW for HR-AR coated devices. For both signs of the strain, strain-compensation applied by oppositely strained barrier and separate confinement layers, results in higher intensity, narrower-linewidth photoluminescence emissions, and reduced threshold currents. Furthermore, the strain compensation is shown to be effective for improving the reliability of strained MQW structures with the quantum wells grown near the critical thickness. Linewidth enhancement factors as low as 2 at the lasing wavelength were measured for both types of strain. Distributed feedback lasers employing either compressively or tensile strained InGaAsP-InP MQW active layers both emit single-mode output powers of over 80 mW and show narrow linewidths of 500 kHz.<
>