Flashover voltage of alumina ceramic contaminated by metal vapor in vacuum interrupters

We investigated the influence of metal vapor contamination of ceramic surfaces on flashover voltage (FOV) in vacuum. First, disk shape alumina (Al/sub 2/O/sub 3/) ceramics with surface resistivity (/spl rho/) of 10/sup 2/-10/sup 15/ /spl Omega/ were produced using deposition phenomena of metal vapor emitted from CuCr contacts. The impulse FOV for the ceramics decreased, as /spl rho/ reduced; FOV, the conditioning effect on FOV, and the scattering of FOV decreased when /spl rho/ was below 10/sup 12/ /spl Omega/. Therefore, the criterion value /spl rho/, which maintains excellent flashover performances of ceramic surface, is 10/sup 12/ /spl Omega/. Second, experimental vacuum interrupters (VIs) were produced to measure breakdown voltage before and after forty short-circuit current switchings with 20-40 kA/sub rms/ and were disassembled to measure the /spl rho/ of their inner ceramic surface. In a VI, which has inside diameters at both ends of the main shield much larger than the contact diameter, /spl rho/ was reduced to 10/sup 4/ /spl Omega/, further decreasing breakdown voltage between terminals.