Hg1-xCdxI2 20–25-μm-thick layers with a uniform composition in the range of x=0.1–0.2 were grown on CdTe substrates by vapor phase epitaxy (VPE). The growth was carried out using an α-HgI2 polycrystalline source at 200 °C and in the time range of 30–100 h. The layers were studied by scanning electron microscopy (SEM) and high resolution synchrotron x-ray topography (SXRT). The SEM and SXRT images of Hg1-xCdxI2 VPE layers allow one to identify the defects affecting the layer structure. The two main types of structural defects in the layers are subgrain boundaries and densely spaced striations similar to those referred generally to as vapor grown HgI2 bulk crystals. The effect of the growth time on these defects has been analyzed and on the basis of this it has been possible to grow Hg1-xCdxI2 layers with low defect density.© 1997 American Institute of Physics.
A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.