Optical detection of magnetic resonance in nitrogen vacancy centre ensembles in bulk diamond using an off-resonant probe laser beam

Nitrogen vacancy (NV) centres are a type of defect in diamond that exhibit a number of interesting properties. NV centres can be optically excited around 450-650 nm and emit fluorescence at around 550-800 nm [1]. The optical excitation also spin polarises the negatively charged NV centres, permitting optical detection of magnetic resonance [2]. This allows nanotesla scale sensitive magnetometry to be performed with nanometre scale spatial resolution [3].To date, a direct measurement of stimulated emission from ensembles of NV centres in diamond has yet to be demonstrated experimentally. Despite this, stimulated emission depletion microscopy has been utilised in superresolution imaging that relies on the stimulated emission of single NV centres to quench fluorescence [4]. Recently, there has also been similar indirect experimental evidence of stimulated emission in NV ensembles [5]. We thus aimed to show both optical gain of a probe beam in a pumped NV-rich diamond sample and a modulation of this gain via microwave excitation of its ground level spin transitions. The experimental set-up consisted of a pump (532 nm) and probe (723-950 nm) laser beam combined with a dichroic mirror and focused into a bulk diamond specimen to a spot-size of around 90 microns. Pump excitation powers of up to 3 W and probe powers up to 0.5 W were used. The beams were then collimated and separated with a prism and the probe power measured with a photodiode. The diamond specimen was placed on an antenna to allow simultaneous excitation with microwaves. A double modulation scheme was employed to measure either the change in probe power due to the pump laser or the microwave excitation during any one experiment.