Thermal degradation of transformer pressboard impregnated with magnetic nanofluid based on transformer oil

In this paper, the thermal ageing of pressboard impregnated with two kinds of insulation liquids is studied by means of frequency domain spectroscopy which involves the measurement of real and imaginary part of complex permittivity as function of frequency. The magnetic nanofluid was composed by mineral transformer oil as carrier liquid, nanoparticles of magnetite and surfactant. The thermal aging test was performed at the temperature 90°C for 1000 hours. Each sample had two variations, with and without copper, which has function catalyst. Then frequency domain spectroscopy was investigated at 40°C for restriction of moisture influence from surrounding. From the data and curves, it can be shown that the undried samples are dried with the aging time and cooper considerably getting worse the imaginary part of complex permittivity. In case of magnetic nanofluid, the colloidal suspension was unstable after 800 hours of the thermal ageing. There was found much more resistance of moisture at the nanofluids than in case of mineral oil impregnated pressboard.