The implementation of hybrid bonded permanent magnet on permanent magnet generator for renewable energy power plants

This paper describes application of permanent magnet on permanent magnet generator (PMG) for renewable energy power plants. Permanent magnet used are bonded hybrid magnet that was a mixture of barium ferrite magnetic powders 50 wt % and NdFeB magnetic powders 50 wt % with 15 wt % of adhesive polymer as a binder. Preparation of bonded hybrid magnets by hot press method at a pressure of 2 tons and temperature of 200°C for 15 minutes. The magnetic properties obtained were remanence induction (Br) =1.54 kG, coercivity (Hc) = 1.290 kOe, product energy maximum (BHmax) = 0.28 MGOe, surface remanence induction (Br) = 1200 gauss, density = 3.83 g/cm3, and curie temperature of 400°C. Magnet samples were implemented on PMG at speed of 100–600 rpm. The maximum power at nominal speed was 93 Watt.