Comparison of Direct Growth and Wafer Bonding for the Fabrication of GaInP/GaAs Dual-Junction Solar Cells on Silicon

Two different process technologies were investigated for the fabrication of high-efficiency GaInP/GaAs dual-junction solar cells on silicon: direct epitaxial growth and layer transfer combined with semiconductor wafer bonding. The intention of this research is to combine the advantages of high efficiencies in III-V tandem solar cells with the low cost of silicon. Direct epitaxial growth of a GaInP/GaAs dual-junction solar cell on a GaAs
_y
P
_1-y
buffer on silicon yielded a 1-sun efficiency of 16.4% (AM1.5g). Threading dislocations that result from the 4% lattice grading are still the main limitation to the device performance. In contrast, similar devices fabricated by semiconductor wafer bonding on n-type inactive Si reached efficiencies of 26.0% (AM1.5g) for a 4-cm
²
solar cell device.