Electrical and chemical characterization of W/sub 1-x-y/Si/sub x/N/sub y/ (0/spl les/x/spl les/0.42, 0/spl les/y/spl les/0.30) Schottky diodes for self-aligned gate GaAs MESFETs

WSiN Schottky diodes on GaAs have been electrically and chemically characterized for atomic silicon and nitrogen; compositions of 0 to 42% and 0 to 28%, respectively. It is found that the main cause for Schottky diode degradation, after high temperature annealing, is the out-diffusion of As from GaAs. For films with atomic nitrogen composition of /spl ges/5%, As outdiffusion is eliminated as long as the atomic Si composition is /spl les/40%. WN films (5% nitrogen) were applied to the fabrication of self-aligned gate lightly doped drain MESFET's with buried P layer. A maximum transconductance, g/sub m/, of 370 mS/mm, f/sub T/ of 33 GHz, and DCFL inverter delay of 29 ps are measured for a 0.5 /spl mu/m gate technology.<
>