Mobility enhancement in TaN metal-gate MOSFETs using tantalum incorporated HfO/sub 2/ gate dielectric

TaN metal-gate nMOSFETs using HfTaO gate dielectrics have been investigated for the first time. Compared to pure HfO/sub 2/, a reduction of one order of magnitude in interface state density (D/sub it/) was observed in HfTaO film. This may be attributed to a high atomic percentage of Si-O bonds in the interfacial layer between HfTaO and Si. It also suggests a chemical similarity of the HfTaO-Si interface to the high-quality SiO/sub 2/-Si interface. In addition, a charge trapping-induced threshold voltage (V/sub th/) shift in HfTaO film with constant voltage stress was 20 times lower than that of HfO/sub 2/. This indicates that the HfTaO film has fewer charged traps compared to HfO/sub 2/ film. The electron mobility in nMOSFETs with HfO/sub 2/ gate dielectric was significantly enhanced by incorporating Ta.