Low-resistance ultrashallow extension formed by optimized flash lamp annealing

Flash lamp annealing (FLA) technology is proposed as a new method of activating implanted impurities. By optimizing FLA and implantation conditions, junction depth (Xj) at the concentration of 1 /spl times/ 10/sup 18/ cm/sup -3/ and the sheet resistance of 13 nm and 700 /spl Omega//sq for As and 14 nm and 770 /spl Omega//sq for BF/sub 2/ with junction leakage lower than 1 /spl times/ 10/sup -16/ A//spl mu/m/sup 2/ at 1.5 V were successfully obtained without wafer slip and warpage problems.