Tracking and erosion of HTV silicone rubbers of different thickness

Tracking and erosion behaviors of high temperature vulcanized (HTV)-silicone rubber (SIR) of 0.5 to 6.0 mm thicknesses were investigated in order to obtain the optimum thickness for enhancing tracking and erosion resistance under various leakage current levels. Under low leakage current, thinner samples showed a higher tracking and erosion resistance, while under medium and high leakage current, thicker samples showed better resistance to these behaviors. The optimum thickness to prolong the time to tracking and erosion failure appeared in the range of 1.0 to 3.0 mm thickness. The content of an initial low molecular weight (LMW) silicone fluid was shown to be closely related to the development of leakage current and high temperature thermal spots. The results indicate that the sample thickness is crucial to the ability of HTV-SIR to withstand a large number of high temperature thermal spots under condition of high level leakage current.