Fabrication and characterization of high-speed polyurethane-disperse red 19 integrated electrooptic modulators for analog system applications

The fabrication and characterization of polymeric electrooptic modulators, made of a thermally crosslinkable polyurethane with Disperse Red 19 side chains, are summarized in this paper. Straight channel and Mach-Zehnder modulators have been fabricated, packaged and tested for the fiber-optic analog transmission system applications. Device performances including halfwave voltage, insertion loss, on-off ratio, and modulation frequency responses were measured. Long-term halfwave voltage stability, dc-bias voltage stability, and optical power handling capability at 1.3-/spl mu/m wavelength were investigated. A carrier-to-noise ratio of 53 dB and 80-channel television transmission have been demonstrated using the packaged polymer modulators.