Switching performance of AgW-Ag(Sn,In)O and AgW-AgSnO/sub 2/ contact pairs

Experiments were conducted to determine the switching performance of Ag-W contacts when operated in combination with Ag-(Sn,In)O and Ag-SnO/sub 2/ materials. Contact pairs for each combination were evaluated in an experimental actuator at a current of 150 A. The Ag-W contact was always the moving contact. The new contacts were closed, a steady current of 150 A was passed, and the voltage drop (V/sub c/) across the contacts and the temperature rise (T/sub r/) of the back of the fixed contact was measured. The contacts then switched a 150-A, 600-V (RMS) circuit for 2000 operations, and the above measurements were repeated. Both the Ag-W versus Ag-(Sn,In)O and the Ag-W versus Ag-SnO/sub 2/ contact pairs gave low values of V/sub c/ when new, a characteristic of good Ag to Ag contact. After 2000 operations, the V/sub c/ values for both contact combinations were very high and variable. Metallurgical examination of the contacts showed arc-resistant oxide surfaces containing complex oxides of Ag, Sn, and In alloys as well as complex tungstates formed from combinations of Ag, Sn, and In.<
>