Effect of ion-irradiation induced defect on the optically active Er ions in Er-doped silicon-rich silicon oxide

We found that the initial presence of defects induced by ion-irradiation reduces the fraction of Er ions that can be excited via nanocluster silicon (nc-Si) even after their removal via high-temperature annealing.