High-modal gain 1300-nm In(Ga)As-GaAs quantum-dot lasers

A semiconductor laser containing seven InAs-InGaAs stacked quantum-dot (QD) layers was grown by molecular beam epitaxy. Shallow mesa ridge-waveguide lasers with stripe width of 120 mum were fabricated and tested. A high modal gain of 41 cm
^-1
was obtained at room temperature corresponding to a modal gain of ~6 cm
^-1
per QD layer, which is very promising to enable the realization of 1.3-mum ultrashort cavity devices such as vertical-cavity surface-emitting lasers. Ground state laser action was achieved for a 360-mum-cavity length with as-cleaved facets. The transparency current density per QD layer and internal quantum efficiency were 13 A/cm
²
and 67%, respectively